PRODUCTS
 
HILAM HP -200
 
HILAM HP-200 + HP-200H is highly versatile of two component solvent based polyurethane adhesive for High performance laminates of various films including OPP, PET, Nylon, Cellophane, ,PS ,PVC ,FOIL,LLDPE ,PVDC Coated film and paper .It offers excellent chemical and heat resistance with very high bond strength and especially provides excellent performance for boil , hot fill and retort packaging.
And it also provides excellent performance for extrusion lamination /anchor coating.
PHYSICAL PROPERTIES HILAM GP-100 HILAM GP-100H
Product Description Main Adhesive Hardener (Curing Agent)
Solid Contents 80 ± 2% 75 ± 2%
Appearance Colourless to Pale Yellow Colourless to Pale Yellow
Typical Properties OH. NCD
Viscosity by Brook Filed Viscometer (LVT )25 C 2000-40000 1000-2000
Diluents Ethyl Acetate Ethyl Acetate
Clarity Clear Clear
Odour Odouless once dried Odouless once dried
Mixing Ratio 100 part by weight 15 part by weight
Self Life 6 Months 6Months
 
Mixing Ratio :
It is recommended that the mixed adhesive be diluted to a solid content such as
Solid Content (%)
HILAM HP-200
HARDENER HP-200H
ETHYL ACETATE
VISCOSITY Fc B4.5 Sec
TOTAL
30
100
15
122.5
13-14
237.5
35
100
15
88.5
18-19
203.5
40
100
15
63
28-29
178
 
Application Areas
HILAMHP -200 + HP-200H is recommended for high performance lamination, it especially designed for manufacturing of Flexible Packaging use for boil, hot fill, retort, acidic Liquids, chemicals, paste pouching and aggressive goods packed in film to film and film to foil lamination.
 
Application Guide
Coating Method: HILAM adhesive is applied on all dry laminating machines with gravure roll coating or cylinder coating
 
Drying Temperature
With Dry chamber temperature or drying web temperature of 65 0C-900C and combining with Nip roll temperature of 65 0C-900 C are recommended to completely remove the solvent carrier.
Ensure complete removal of solvent .To prevent retention, drying condition has to be adjusting to substrate, application weight and machine speed.
High laminating temperatures together with high line pressure of calendar improve the bond strength and optimal appearance of laminated properties.
 
Coating weight /Deposit weight
a) Coating Weight for Dry Lamination
For normal applications the dry adhesive coating weight may range from 2-2.5 gsm on the film or foil combination and the end use of the laminates. However for the specific application like in ticker / porous substrate (such as paper and board), higher coating weight of dry adhesive is recommended.
If the coating weight of the adhesive which is coated on films is too small ,that the appearance will not be clear as like bubble ,floating, roll mark, the bonding strength is not enough either and just the opposite if the coating weight is too-much ,that the blur tunneling ,wrinkle ,shrinkage etc.
Substrate
Unprinted or lightly webs
Heavily printed webs or thicker substrate
Recommended dry Adhesive Deposit
2 – 2.5 gsm
up to 3-4.5 gsm
   
b) Coating weight for extrusion coating lamination
The adhesive coating weight may range from 1.0 -1.5 gsm
 
Speed Line
Fastest line speed 60-150 m/min

Aging Time
48 hours at approx 50 0C – 600Cat aging room for snack foods or dry products .72-96 hours at 50 0C – 600Cat aging room for boil and retort packaging.

Curing Time
The laminate can be processed rewound and slit after 1-2 days for triplex laminates is possible 24 Hours after duplex production. Good lamination bond are achieved within 7-12 days after laminating of storage at room temperature.

Use recommendation

The bonding strength makes a difference according to each film, even the sources materials of film are same, but their bonding strength can be quite different and beside additives and slip agents on polyethylene and polypropylene film, aggressive ingredients, printing inks, corona treatment and film coating are significant importance for the final performance properties.
All the polyolefin films must be treated prior to lamination and treated surface to be used for lamination .The recommended level is 38 ̴ 40dynes/ cm to achieve minimum required surface wet ability level.
Since the ingredients in films and Inks may interfere with the good performance of this adhesive, customers are strongly recommended to carefully test HP-200 + HP-200H before using it in production, to check its suitability for each and every end use requirement.

Pot Life
The pot Life of mixed adhesive is 12-14 hours depending on the temperature and the quantity of the mixture.

Cleaning
The application system of the equipment should be cleaned with solvent after every operation. Special care should be taken to avoid adhesives drying and curing in the cells of the gravure application cylinder.

Storage /Caution & Safety
The adhesive and hardener must not be stored in direct sunlight or flame or spark source and stored in the place where cool, dry and well ventilated and keep stored in the original unopened and undamaged container. Opened containers of the material have to be closed immediately and the material should be consumed within a short period .Avoid contact with skin & eyes .Safety regulations with regard to handling of
Material, material safety data sheet to be followed.

Standard packing
HILAM HP-200 is available in 200 kg Barrel packing and in 50 kg barrel and HP -200H in 24 kgs pail & 6 kg cans.

 
 
 
|
|
|
|
                 